Chlorinated rubber anti-fouling boat paint
Chlorinated rubber anti-fouling boat paint
Front
Reverse
Technical Parameters
| Property | Solvent based ( Oil based ) |
| Thickness | 40mu/layer |
| Theoretical coverage | 0.2kg/㎡/layer |
| Recoating time | ＜2h（25℃） |
| Drying time (hard) | >24h （25℃） |
| Service life | > 15 years |
| Construction tempature | >8℃ |
| Paint colors | Black |
| Application way | Spray, roll, brush |
| Storage | 5-25℃, cool, dry |
Application Guidelines
Pre-treated substrate
Aluminum chlorinated rubber primer
Chlorinated rubber anti-fouling paint
| Application Scope | |
| Suitable for protection of the ship bottom and some dock buildings. | |
| Package | |
| 20kg/barrel. | |
| Storage | |
| This product stored at above 0 ℃, well ventilation, shady and cool place. |
Fashion
In addition to its functional benefits, chlorinated rubber anti-fouling boat paints also offer style. Available in a variety of colors, this paint can be used to match or complement a boat's existing color scheme. Using this paint, boat owners can give their boat a new look while enhancing its performance.
All in all, chlorinated rubber anti-fouling boat paints are an excellent choice for boat owners who want to protect their boats and enhance their performance. The paint is extremely durable, stain-resistant, easy to apply and available in a variety of stylish colours. With these features and benefits, it's not hard to see why chlorinated rubber anti-fouling boat paints are so popular among boat owners and hobbyists.
Application Instruction
Construction Conditions
The construction conditions should not be in moisture season with cold weather (temperature is ≥10℃ and humidity is ≤85%). The below application time refers to normal temperature in 25℃.
Application Step
Surface preparation :
The surface should be polished, repaired, dust collected according to the site basic surface condition; Correct substrate preparation is critical for optimum performance. Surface should be sound, clean, dry and free from loose particles, oil, grease, and other contaminants.
Aluminum chlorinated rubber primer:
1) Mix ( A ) primer, ( B ) curinge agent and ( C ) thinner in a barrel according to ratio by weight;
2) Fully mix and stir in 4-5 min until without equal bubbles, ensure paint be fully stirred.The main purpose of this primer is to reach the anti-water,and seal the substrate completely and avoid air-bubbles in the body coating;
3) The reference consumption is 0.15kg/m2. Rolling, brush or spray the primer evenly (as the attached picture show) by 1 time;
4) Wait after 24 hours, the next application step to coat the chlorinated rubber anti-fouling paint;
5) After 24 hours, according to the site condition, polishing can be done, this is optionally;
6) Inspection: ensure the paint film is evenly with uniform color, without hollowing.
Chlorinated rubber anti-fouling top coating:
1) Mix ( A ) top coating, ( B ) curinge agent and ( C ) thinner in a barrel according to ratio by weight;
2) Fully mix and stir in 4-5 min until without equal bubbles, ensure paint be fully stirred;
3) The reference consumption is 0.35kg/m2. Rolling, brush or spray the primer evenly (as the attached picture show) by 1 time;
4) Inspection: ensure the paint film is evenly with uniform color, without hollowing.
Cautions
1) The mixing paint should be used within 20 minutes;
2) Maintain 1 week, can be used when paint is solid absolutely;
3) Film protection: keep away from stepping on, rain, exposing to sunlight and scratching until the film is fully dried and solidified.
Notes
The above information is given to the best of our knowledge based on laboratory tests and practical experience. However, since we cannot anticipate or control many conditions under which our products may be used, we can only guarantee the quality of the product itself. We reserve the right to alter the given information without prior notice.
Conclusion
Practical thickness of the paints can be little different from the theoretical thickness mentioned above due to many elements like environment,application methods,etc.